Nanocrystalline materials

ABSTRACT

Glass or crystal particles of nanocrystalline size having a minor dimension of 0.1 to 100 Angstrom units. They may be prepared by controlled thermal separation of phase-separable glasses. Preferred crystal forms are zinc pyrophosphate and lithium disilicate. A crystallizable glass is combined with phyllosilicate particles and sintered to form an oriented composite body. During slow sintering, the crystal grows epitaxially on the phyllosilicate.

FIELD OF THE INVENTION

The field is glass and glass-ceramic materials in particulate form.

BACKGROUND OF THE INVENTION

The invention relates to glass and glass-ceramic particles ofnanocrystalline size. It is further concerned with methods of producingmaterials of such minute particle size.

The term "nanocrystalline" refers to particles having a diameter orthickness on the order of a nanometer. More particularly, it is hereused to refer to particles in the size range of 0.1 to 100 Angstromunits. Such minute particles are characterized by large surface areas,as measured by the nitrogen absorption (BET) method.

Particles of nanocrystalline size are of interest in diverseapplications. In general, they react with each other, or with othermaterials, at lower temperatures than are normally required for the samereaction of such materials in a bulk state. Thus, they are of particularvalue in forming composite materials with either organic or inorganicreactants.

It is known to delaminate phyllosilicate materials to produce plateletsof nanocrystalline size. It is a purpose of the present invention toprovide particles of corresponding size from glass and glass-ceramicmaterials.

SUMMARY OF THE INVENTION

The material aspect of my invention is glass, or glass-ceramiccrystalline, particles in the size range of 0.1 to 100 Angstrom units.It further resides in inorganic, or inorganic-organic, compositematerials produced from such particles. A particular embodiment is amaterial embodying phosphorous-nitrogen bonding and resulting fromreacting an ammonium compound with phosphate glass particles.

The invention further resides in a method of producing glass, orglass-ceramic crystalline, particles in the size range of 0.1 to 100Angstrom units. The method comprises providing a precursorphase-separable glass, preferably a phosphate glass capable of beingseparated into a stable crystalline or glassy phase and a soluble matrixphase, separating the precursor glass into two phases at a ratecontrolled to favor small particle formation of a stable glass orcrystal phase, and solubilizing the matrix, to leave the stable phase inparticulate form. In one embodiment, the glass is crystallizable and acrystal phase is separated by heating at the low end of itscrystallizing temperature range to provide a fine crystalline phase. Inother embodiments, the particles formed are reacted with an ammonium andor a halide compound.

PRIOR ART

It is known from my prior United States patents to delaminatephyllosilicates to particle sizes below 1000 Angstrom units and as smallas unit cell size.

No. 4,826,628 describes heating a phyllosilicate in a reactive vaporphase, preferably hydrogen-containing; No. 4,952,388 describes an acidtreatment; No. 4,836,954 describes fluorinating a phyllosilicate byreaction with a compound such as NH₄ HF₂ ; No. 4,676,929 describestreating a phyllosilicate with an aminocarboxy acid to delaminate andproduce a gel.

It is also well known in the glass art to separate a glass into phasesof differing solubilities, and to remove the soluble phase to produce aporous glass composed of the stable phase. An early disclosure of thisprocedure, as used with phase-separable borosilicate glasses, is foundin U.S. Pat. Nos. 2,215,039 and 2,286,275 (Hood borosilicate glasscontaining 5-15% Al₂ O₃ and 7-24% P₂ O₅.

U.S. Pat. Nos. 4,233,169 and 4,395,271 (Beall et al.) describe producingporous bodies of magnetic glass and/or crystal-containing materials withmagnetic crystals. The bodies are produced by phase-separation, followedby acid etching of a soluble phase.

U.S. Pat. No. 3,650,721 (Hammel et al.) describes a process of phaseseparation and leaching to produce micro-porous fibers and granules forsmoke filters that have a minor axis length of 0.5 to 1000 microns.

DESCRIPTION OF THE INVENTION

The present invention provides crystalline particles of nanometerdimensions from precursor glasses and glass-ceramics. It is particularlyconcerned with platey-type crystals having high aspect ratios. These aresimilar in nature to particles obtained by delaminating phyllosilicateminerals such as vermiculite.

Nanocrystalline particles are characterized by high surface areas thatmay be several times greater than surface areas on larger size particlesof the same composition. Such nanocrystalline size particles may exhibitexcellent thermal and chemical stabilities over a wide range ofstoichiometries. Because of their minute size and geometry, they tend topack tightly and sinter to near theoretical density after pressing orextrusion.

The invention further relates to generation of improved chemical andphysical properties in such materials via diffusion reactions. Thesereactions occur during thermal, gas phase treatments of thenanocrystalline materials. In particular, unique reactions occur withphosphorus-containing materials, such as phosphate glass-ceramics. Also,treatment of phosphate glass particles with anhydrous ammonia hasproduced substantial improvement in durability and thermal stability.Fourier Transform-Infra Red (FT-IR) analyses have shown P-N bonding as aresult of such reactions.

It is also possible to generate new phosphate material stoichiometriesas a result of reactions with various aqueous hydrogen ion-containingreactants. These include such reactants as NH₄ HF₂, NH₄ HF and C₂ H₇ O₂N. Substantial amounts of halide ions may be introduced by reaction withthe ammonium halides.

In addition to diffusion-altered phosphates, as noted above, an area ofparticular interest is superplastic ceramic composites. Also, ofinterest for filtration and for biomedical applications, are materialswith extremely fine pores. Another application is low densitymicrofoams.

Nanocrystalline materials may be obtained from phase separated glasseswherein the separated phase is either a second glassy phase or acrystalline phase. In either case, a soluble glass matrix is providedthat can be readily leached to leave the more stable glass or crystalparticles.

In the case of the crystallized glass, that is, a glass-ceramic, finecrystals are obtained by so controlling the nucleation and crystallizingheat treatment that numerous nuclei develop. In general, fine crystaldevelopment is favored by inducing crystal growth at the lower end ofthe temperature range within which crystallization occurs, whichpractice requires longer heat treatment times. This heat treatment atlow temperatures causes a greater number of nuclei to form, resulting inmany small, fine crystals, rather than fewer, large crystals to develop.

The invention is further described with respect to certain specificembodiments which are presently considered to be the best mode ofpractice.

TABLE I sets forth compositions, in percent by weight as calculated fromthe glass batch, for crystallizable phosphate glasses. Thesecompositions were formulated to provide a pyrophosphate crystal phase,in particular, zinc pyrophosphate, when heat treated. Batches wereprepared from conventional materials and melted in crucibles for 4 hoursat 1200° C. Each glass melt was quenched to provide a clear glass thatcould be crystallized by a controlled heat treatment.

                  TABLE I                                                         ______________________________________                                                Example                                                                       1           2      3                                                  ______________________________________                                        P.sub.2 O.sub.5                                                                         46.5          50.0   47.9                                           ZnO       32.8          37.0   35.8                                           Al.sub.2 O.sub.3                                                                        2.4           3.4    2.0                                            SnO       6.9           --     --                                             Li.sub.2 O                                                                              2.2           2.4    1.8                                            Na.sub.2 O                                                                              5.3           5.2    4.3                                            K.sub.2 O --            --     6.6                                            S.A.      2.4           1.1                                                   ______________________________________                                         S.A. indicates surface area in square meters per gram (m.sup.2 /gm) as        measured by BET nitrogen absorption.                                     

Each of the glasses was heat treated to cause crystallization of a zincpyrophosphate crystal phase in a glassy matrix. Crystallization couldoccur over a range of 300 ° to 600° C. with times varying from one-halfhour at the high end of the range to as long as ten hours at the lowend. In general, finer crystals are obtained with lower temperatures forlonger times.

Each glass-ceramic thus produced was then exposed to different vaporphase reactions to determine the effect of such treatment. Thesetreatments were at temperatures adapted to provide the reactant materialemployed in a vapor phase form. Thus, ammonium acid fluoride (NH₄ HF)was employed at temperatures on the order of 125°-135° C. for timesranging up to four hours.

Thereafter, the crystals were chemically analyzed to determine gasesdiffused into the crystal. Also, surface areas were measured to comparewith the precursor.

TABLE II shows the vapor phase treatments for each example of TABLE I,together with the changes effected by such treatments:

                  TABLE II                                                        ______________________________________                                        Ex.     Vapor Phase                                                                              S.A.     H   N     F    Cl                                 ______________________________________                                        1       NH.sub.4 HF.sub.2                                                                        15.5     --  3.7   7.9  --                                 1       NH.sub.4 HF                                                                              9.2      --  4.2   7.0  --                                 1       NH.sub.4 Cl                                                                              16.6     --  1.5   --   0.2                                1       Control    2.4      --  0.1   0.0  --                                 2       NH.sub.4 HF.sub.2                                                                        17.6     --  4.4   8.3  --                                 2       NH.sub.4 HF                                                                              11.2     --  5.3   8.2  --                                 2       NH.sub.4 Cl                                                                              6.9      --  0.5   --   0.0                                2       Control    1.1      --  0.1   0.0  --                                 3       NH.sub.4 HF.sub.2                                                                        13.3         3.7   10.7 --                                 3       NH.sub.4 HF                                                                              11.7     1.6 4.7   8.3  --                                 3       NH.sub.4 Cl                                                                              17.3     1.3 3.3   --   0.7                                3       C.sub.2 H.sub.7 O.sub.2 N                                                                22.0     1.7 4.3   --   --                                 3       Control                                                               ______________________________________                                    

TABLE III sets forth, in weight percent calculated on an oxide basis,compositions of glasses that were crystallized, as described above, toglass-ceramics having crystals of nanocrystalline size;

                  TABLE III                                                       ______________________________________                                               Example                                                                       4           5       6                                                  ______________________________________                                        SiO.sub.2                                                                              58              47.5  --                                             B.sub.2 O.sub.3                                                                        --            11      --                                             Al.sub.2 O.sub.3                                                                       26.4          29       1.5                                           Bi.sub.2 O.sub.3                                                                       --            --      52.3                                           P.sub.2 O.sub.5                                                                         8.16         --      --                                             MgO      1.4           --      --                                             CaO      --            --       9.7                                           SrO      --            --      18.0                                           ZnO      --            10      --                                             CuO      --            --      18.5                                           ZrO.sub.2                                                                              2.4           --      --                                             TiO.sub.2                                                                              3.1           --      --                                             Na.sub.2 O                                                                              0.14         --      --                                             K.sub.2 O                                                                              --             2      --                                             F        0.4           --      --                                             Cr.sub.2 O.sub.3                                                                       --              0.1   --                                             As.sub.2 O.sub.5                                                                       --              0.4   --                                             ______________________________________                                    

Each of Examples 4-6 was reduced to particulate form preparatory tofurther treatment.

Example 4 was exposed to a 4 molar solution of NH₄ HF₂, washed twicewith distilled water and dried at 150° c. Chemical analysis of the driedmaterial showed only minor changes in the original constituents, exceptfor silica and P₂ O₅. The amounts of these oxides were reduced to 19.5%and 3.0%, respectively. Meanwhile, nitrogen and fluorine contents of8.6% and 36.8%, respectively, were observed in the analysis.

Example 5 was treated in the same manner as Example 4, except for athird washing before drying. The analysis of this material, aftertreatment, showed a N content of 2.5% and a F content of 9.3%.Measurement of surface area showed a value of 32.2 m² /gram.

Samples of Example 6 were treated with 4 molar solutions of NH₄ HF₂, NH₄F and NH₄ Cl. Analyses of the treated samples showed the followingvalues:

                  TABLE IV                                                        ______________________________________                                        NH.sub.4 HF.sub.2  NH.sub.4 F                                                                            NH.sub.4 Cl                                        ______________________________________                                        N       <0.05           0.24    0.34                                          F       18.7           17.2    --                                             Cl      --             --      11.1                                           S.A.    26.6           41.4    69.9                                           ______________________________________                                         S.A. = surface area.                                                     

I have further found that composite bodies, capable of sintering to fulldensity, can be made by extruding and sintering combinations of highaspect ratio phyllosilicates and glasses that crystallize at lowtemperatures to glass-ceramics having a circular or bladed morphologies.Preferably, the phyllosilicates have aspect ratios of at least 5:1. Theresulting sintered composite bodies have excellent gas permeability anddielectric properties and moderate coefficients of thermal expansion,exhibit excellent toughness, and are relatively inexpensive to producebecause of low melting and processing temperatures.

The preferred phyllosilicate to employ is talc or vermiculite that hasbeen exposed to a vapor phase reaction such as described in my U.S. Pat.Nos. 4,826,628 and No. 4,836,954. These materials have surface areas of7 and 12 m² /gram, respectively.

Both lithium disilicate and alkaline earth metal silicate glasses thatcrystallize to glass-ceramics during sintering have been employed to mixwith the phyllosilicates. A preferred lithium disilicate glass iscomposed of, in calculated weight percent: 70.7% SiO₂, 4.5% Li₂ O, 4.2%K₂ O, 2.8% Na₂ O, 4.6% Al₂ O₃ and 3.2% B₂ O₃.

Extrusion experiments were performed with 25:75, 50:50, and 75:25 byweight combinations of glasses and phyllosilicates. The best crystalorientation and sintering densities in the sintered bodies were obtainedwith the 50:50 mixes. Numerous dewaxing and sintering thermal cycleswere evaluated employing heating rates varying from 50° C. to 1200°C./hr. Best results were obtained with slow heating rates and a toptemperature of about 900° C.

The vapor phase treated talc or vermiculite was combined with sixdifferent lithium disilicate glasses to produce mixtures for ribbonextrusion trials. It was found possible to extrude ribbon with a 10:1drawdown ratio by using a 50:50 combination of treated vermiculite withthe lithium disilicate glass noted above. The extruded ribbons were0.0015" (0.04 mm) thick and 0.75" (1.9 cm) wide, and had excellent greenstrength, that is, pre-sintered strength.

Diamond indentation toughness measurements on the sintered bodiesrevealed that the epitaxially extruded, vermiculite-glass ribbons, whenstacked and sintered to form bars, produced bodies having toughnesscharacteristics comparable to alumina and canasite glass-ceramics.Sintered grain size was observed to be in the three to five micronrange. Surface x-ray diffraction data showed excellent phyllosilicatebasal orientation within the sintered ribbons with 80% intensity at the002 line, as compared to 14% in an unextruded powder control. A numberof the sintered composites were observed to have an extremelyfine-grained microstructure with basal cleavage and an interlocking typestructure.

By way of further illustrating the properties of the extruded, sinteredbars, a series of varied property measurements was made on a bodyprepared from a 50-50 mixture of vermiculite and a glass having acomposition approximating that of lithium disilicate. The recordedmeasurements are set forth in TABLE V together with correspondingmeasurements on alternative materials commercially available. Hardnessis given in Knoop values obtained with a 100 gram weight. Toughness ismeasured in ergs/cm² at 298° K. with a standard four point suspension,and the value is the point on the curve at which brittle fractureoccurs. Dielectric constant is measured at 25° C. and 1 M Hertz, whilevolume resistivity is measured in ohm-cms at 25° C. Permeability is tohelium at 25° C., and the values are given in terms of (cm³ :mm)/(cm²S:cm.Hg).

                  TABLE V                                                         ______________________________________                                        Hardness                                                                      Canasite glass-ceramic                                                                            600-650                                                   Sintered Al.sub.2 O.sub.3                                                                         1781                                                      Amorphous anorthite  508                                                      Single crystal      2000                                                      Test sample         1000                                                      Toughness                                                                     Glasses             3500-4700                                                 Beta-spodumene glass-ceramic                                                                      17,500                                                    Sapphire            32,000                                                    Test sample         18,000-26,000                                             Dielectric Constant                                                           Beta-spodumene glass-ceramic                                                                      5.5                                                       Test sample         5.0                                                       Volume Resistivity                                                            Beta-spodumene glass-ceramic                                                                      >14 × 10.sup.10                                     Test sample          10 × 10.sup.10                                     Permeability                                                                  96% silica glass    1 × 10.sup.-10                                      Test sample         1 × 10.sup.-12                                      ______________________________________                                    

TABLE VI sets forth several lithium disilicate glass compositions inweight percent as calculated from the glass batch on an oxide basis.

                  TABLE VI                                                        ______________________________________                                               Example                                                                       7    8        9      10     11   12                                    ______________________________________                                        SiO.sub.2                                                                              77.6   78.2     73.6 62.5   70.6 70.6                                Al.sub.2 O.sub.3                                                                       --     --       --   --     --   4.6                                 BaO      --     6.3      5.8  12.3   --   --                                  B.sub.2 O.sub.3                                                                        --     --       --   --     6.4  3.2                                 Li.sub.2 O                                                                             16     15.5     14.6 12.4   14.5 14.5                                ZnO      3      --       --   --     --   --                                  Na.sub.2 O                                                                             --     --       --   --     --   2.8                                 K.sub.2 O                                                                              3.4    --       --   --     8.6  4.2                                 CaO      --     --       2.1  4.5    --   --                                  SrO      --     --       3.9  8.3    --   --                                  ______________________________________                                    

These compositions were formulated as glass batches which were melted bybeing held at 1400° C. for four hours. The melts were quenched and theglass pulverized to an average particle size of 1-2 microns. Thepulverized glass was mixed with a proportionate amount of phyllosilicatein a slurry that was then dried and fired.

Firing temperatures from 300° to 1000° C., and heat-up rates from 25°/hour to 1000° hour, were investigated. Fast rates and higher toptemperatures favored a light, low density, foam-like body, while bodieswith high density were obtained with low rates and/or lower toptemperatures. A basic consideration for high density is to obtain glassflow and wetting of the phyllosilicate prior to crystallization.

I claim:
 1. A crystallized glass nanocrystalline particle which is azinc pyrophosphate, has a minor dimension in the range of 0.1 to 100Angstrom units and has a platey form in which the aspect ratio is graterthan one.
 2. A crystallized glass nanocrystalline particle which is alithium disilicate crystal which has a minor dimension in the range of0.1 to 100 angstrom units, and which has a platey form in which theaspect ratio is greater than one.
 3. A glass or crystallized glassnanocrystalline particle containing phosphorous, having nitrogen bondedto at least a portion of the phosphorous, having a minor dimension inthe range of 0.1 to 100 Angstrom units and having a platey form in whichthe aspect ratio is greater than one.